Louis Metals proudly provides excellent Stainless Steel 440C Bars and Rods in Houston, USA, shipping precision-engineered materials specially designed for performance in extremely demanding applications. SS 440C is renowned for its hardness, great wear resistance, and average corrosion resistance. Our products are in accordance with ASTM and aerospace-grade specifications, with applications in automotive, tools & dies, and mechanical engineering. With top-of-the-line manufacturing plants and quality control, Louis Metals guarantees you get high-performance rods and bars designed for durability and strength.
Stainless Steel 440C has a typical composition of 16.0–18.0% Chromium and 0.95–1.20% Carbon and is the highest carbon stainless steel within the 400 series. It has a heat-treated hardness of up to 60 HRC and has a tensile strength of 760–1965 MPa. It has excellent wear and abrasion resistance but less corrosion resistance compared to austenitic grades. The alloy is magnetic and best for hardened, polished, or precision-ground parts.
| Specification | ASTM A479/ SA479 ASTM A276/ ASME SA276 |
|---|---|
| Grade | Stainless Steel 440C (UNS S44004) |
| Hex Bar size | 18 to 57mm (11/16″ – 2-3/4″) |
| Round bar size | OD 4mm to 500mm |
| Square bar size | 18mm to 47mm (11/16″- 1-3/4″) |
| Billet Size | 1/2″- 495mm Dia. |
| Rectangles Size | 33 x 30mm – 295 x 1066mm |
| Bright Bar | OD 4mm to 100mm |
| Tolerance | K12 H12, K10, H9, H11, H8, H13K9, H10, K11, or as per need |
| Flat bar size | 1/2” to 10” in thickness of 2 to 150mm |
| Angle bar size | 3*20*20~12*100*100 |
| Finish | centreless ground, Cold (bright) drawn, hot rolled, peeled, smooth turned, hot rolled annealed, slit rolled edge, Bright, Rough Turned, Grinding, Polish & Black |
| Form | Flat Bar, Hollow, Round, Square, Triangle, Rectangle, Half Round Bar, Rod, T-Bar, Precision Ground Bar, Hex (A/F), Blocks, Channel Bar, Threaded, Round Rod, Billet, Profiles, I/H Bar, Ingot, Rings, Forging etc. |
| Technique | 440C Stainless Steel Hot Rolled, Cold Drawn, Rod, Forged Round Bar, Cold Rolled |
| Condition | annealed, Hardened & tempered |
| Section | 3.0 -12.0 mm thickness, 80 x 40 to 150 x 75mm section |
| Channel Bar | 5.0 – 6.0mm thickness |
| Surface | Bright, Cold Drawn, Hot Rolled Pickled, Sand Blasting Finished, Polished, Hairline |
| Hollow Bar | 32mm OD x 16mm ID – 250mm OD x 200mm ID |
|
SS 440C |
Min |
Max |
|---|---|---|
|
Si |
– |
1.00 |
|
C |
0.95 |
1.20 |
|
Mo |
0.00 |
0.75 |
|
P |
– |
0.04 |
|
Ni |
– |
1.00 |
|
Mn |
– |
1.00 |
|
Cr |
16.00 |
18.00 |
|
S |
0.15 |
0.03 |
|
Element |
SS 440C |
|---|---|
|
Tensile (UTS)N/mm² |
1965 |
|
Temp°C |
20 |
|
Reductionof Area |
10 |
|
Elongation(50.8mm) %) |
2 |
|
0.2% YieldN/mm² |
1896 |
|
HardnessHRc |
57 |
|
STANDARD |
UNS |
WERKSTOFF NR. |
JIS |
|---|---|---|---|
|
SS 440C |
S44004 |
1.4125 |
SUS 440C |
Stainless Steel 440C Bars and Rods are known for their high hardness, achieving up to 58-60 HRC when heat-treated. This makes them ideal for applications requiring excellent wear and abrasion resistance.
Stainless Steel 440C offers good corrosion resistance in mild environments, but for more aggressive conditions (like exposure to saltwater), it is recommended to use more corrosion-resistant stainless steel grades like 316 or 317.
440C Rods and Bars are extensively used in the production of surgical instruments, valve parts, ball bearings, and high-performance knives. Due to their toughness and high hardness, they find application in tooling, molds, dies, and rolling elements. In military and aerospace sectors, it‘s preferred for low–corrosion, high–stress applications. It‘s also applied in gauges, cams, and mechanical seals where there is dimensional stability and toughness required.
We provide products that come with both mill test certificates and third-party test certificates, ensuring the highest standards of quality and compliance.
Louis Metals is a leading manufacturer, supplier, and exporter of high-quality bars, rods, and forgings, catering to various industries in Houston, USA
Copyright 2024 Louis Metals. All rights reserved