Louis Metals provides Carbon Steel EN‑44 bars from Houston, which provide robust solutions for engineering and automotive industries. EN‑44 is a heat-treatable medium-carbon alloy that has excellent toughness, resistance to wear, and shock-absorbing properties. We provide these bars in quenched and tempered conditions to ASTM B446/B447 standards, providing reliable sizing and mechanical properties for industrial applications.
EN–44 has a strength of about 0.90–1.20% carbon and 0.45–0.70% manganese. It has tensile strength of 700–850 MPa with a hardness of about HB 230–290
. The composition of the alloy provides a balance of ductility and strength so that it can resist wear and fatigue.
| Specifications | ASTM B446 / ASTM SB446 |
| size | 2-100mm A/F |
|---|---|
| Square bar size | 4 to 100mm |
| Flat bar size | Thickness: 2 -100mm Width: 10 to 500mm |
| Round bar size | Diameter: 3-~800mm |
| Rectangles Size | 33 x 30mm to 295 x 1066mm |
| Angle bar size | 3mm*20mm*20mm~12mm*100mm*100mm |
| Section | 3.0 to 12.0mm thickness |
| Channel Bar | 80 x 40mm to 150 x 75mm section; 5.0 to 6.0mm thickness |
| Hollow Bar | 32mm OD x 16mm ID to 250mm OD x 200mm ID) |
| Billet Size | 1/2″ to 495mm Diameter |
| Finish | Cold (bright) drawn, centreless ground, hot rolled, smooth turned, peeled, slit rolled edge, hot rolled annealed, Rough Turned, Bright, Polish, Grinding, Centreless Ground & Black |
| Tolerance | H8, H9, H10, H11, H12, H13K9, K10, K11, K12 or as per clients’ requirements |
| Surface | Hot Rolled Pickled, Bright, Sand Blasting Finished, Cold Drawn, Hairline, Polished |
| Condition | Hardened & tempered, annealed |
| Technique | Cold Drawn, Hot Rolled, Forged Round Bar,Cold Rolled, Rod |
| Processing | Bar cutting to 650mm |
| Form | Round, Welding Rod, T-Bar, Rod, Precision Ground Bar, Channel Bar, Square, Flat Bar, Blocks, Round Rod, Hollow, Rings, Rectangle, Hex (A/F), Triangle, Threaded, Profiles, Billet, Ingot, I/H Bar, Half Round Bar, Forging etc. |
| Grade | ||||||
| C% | Si% | Mn% | Cr% | Mo% | W% | |
| EN-1A | 0.007 TO 0.15 | 0.10 | 0.80 TO 1.00 | S | P | – |
| 0.20 TO 0.30 | 0.70 MAX | |||||
| EN-8 | 0.35 TO 0.45 | 0.05 TO 0.30 | 0.60 TO 1.00 | S | P | – |
| 0.06 MAX | 0.06 MAX | |||||
| EN-9 | 0.50 TO 0.60 | 0.05 TO 0.30 | 0.5 TO 0.80 | – | – | – |
| EN-19(V 320) | 0.35 TO 0.45 | 0.10 TO 0.30 | 0.5 TO 0.80 | 0.90 TO 1.40 | 0.20 TO 0.40 | |
| EN-24(V 130) | 0.35 TO 0.45 | 0.10 TO 0.35 | 0.45 TO 0.70 | 0.90 TO 1.40 | 0.20 TO 0.35 | NI |
| 1.3 TO 1.8 | ||||||
| EN-31 R-100 | 0.90 TO 1.20 | 0.10 TO 0.35 | 0.30 TO 0.75 | 1.00 TO 1.60 | – | – |
| EN-36C E-200 | 0.12 TO 0.18 | 0.10 TO 0.35 | 0.30 TO 0.60 | 0.60 TO 1.10 | – | NI |
| 3.0 TO 3.75 | ||||||
| EN-42 | 0.70 TO 0.85 | 0.10 TO 0.40 | 0.55 TO 0.75 | – | – | – |
| EN-44 | 0.90 TO 1.20 | 0.30 | 0.45 TO 0.70 | – | – | – |
| EN-45 F-110 | 50 TO 0.60 | 1.5 TO 2.0 | 0.70 TO 1.00 | – | – | – |
| EN-351 | 0.10 TO 0.20 | 0.35 | 0.60 TO 1.00 | 0.40 to 0.80 | 0.08 to 0.10 | NI |
| 0.60 TO 1.00 | ||||||
| EN-353 | 0.10 TO 0.20 | 0.35 | 0.50 TO 1.00 | 0.75 TO 1.25 | 0.08 to o.15 | NI |
| 1.00 TO 1.50 |
| Grade | HEAT TREATMENT | CORRESPONDING SPECIFICATION | |||||
| Hardening Temperature | Quenching Medium | Tempering Temperature | Brinell Rock well hardness | JAPAN JIS | AISI | POLDI THREAD | |
| EN-1A | – | – | – | – | – | – | – |
| EN-8 | 750-900 | OIL | 150-200 | ||||
| EN-9 | 850-900 | OIL | 200-250 | 55-60 | |||
| EN-19 (V 320) | 900-950 | OIL | 200-225 | 45-55 | SCM 4 | 4140 | |
| EN-24 (V 130) | 830-860 | OIL | 540-680 | 45-55 | SNCM 8 | 4340 | |
| EN-31 R-100 | 820-860 | OIL | 180-225 | 59-65 | |||
| EN-36C E-200 | 780-860 | OIL | 170-210 | 61-63 | SNC 22 | 3415 | |
| EN-42 | 600-700 | DIRECT HARDENING | 40-45 | ||||
| EN-44 | 650-750 | OIL | 150 | 45-50 | |||
| EN-45 | 830-860 | OIL | 470-520 | 50-55 | 9255 | ||
| EN-351 | 850-860 | OIL | 175-200 | 62-64 | |||
| EN-353 | 840-870 | OIL | 150-200 | 62-64 | |||
| Standard | CS EN-9 |
| UNS | – |
| WERKSTOFF NR. | CK55 |
| BS | 070M55 |
| IS | C55 |
| JIS | – |
| EN | EN9 |
| SAE/AISI | 1055 |
Yes, Carbon Steel EN-44 Bars can be heat-treated to improve mechanical properties such as strength and hardness. Common treatments include annealing, quenching, and tempering, depending on application requirements.
Carbon Steel EN-44 Bars are used in manufacturing automotive components, tools, and industrial equipment due to their excellent toughness, wear resistance, and high tensile strength, making them suitable for heavy-duty applications.
Carbon Steel EN-44 Bar offers high tensile strength (~700-850 MPa), excellent toughness, good wear resistance, moderate ductility, and hardness (~230-290 HB), making it suitable for heavy-duty applications.
EN–44 bars find wide application in crankshafts, connecting rods, spindles, gears, bolts, and industrial fasteners. They are most suited to parts that need high impact resistance and dimensional stability. EN-44 alloy is also utilized in agricultural equipment, automotive shafts, and tooling platforms with a need for hardened surfaces under a loading cycle.
We provide products that come with both mill test certificates and third-party test certificates, ensuring the highest standards of quality and compliance.
Louis Metals is a leading manufacturer, supplier, and exporter of high-quality bars, rods, and forgings, catering to various industries in Houston, USA
Copyright 2024 Louis Metals. All rights reserved